AT 192
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZDaXSI_AT-192.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This homopolymer is suitable for use in carpet extrusion coating applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.913 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 220 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 95 | ASTM D2240 | |
| Shaw D | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 8.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 160 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -10.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 71.2 | °C | ASTM D1525 |
| Melting Temperature | 100 | °C | DSC |
| Additional Information |
|---|
| The value listed as Density-Specific Gravity, ASTM D1505, was also tested in accordance with ASTM D1928 ProcC Mod. |
| Note Message | |
|---|---|
| 1 . | Type 4, 50mm/min |
| 2 . | Type 4, 50mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC5800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Shanghai Ofluorine PVDF 9201 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Torelina® A410MX07 | Toray Resin Company | PPS | Torelina® |
| Edgetek™ NN-50GF/000 | PolyOne Corporation | Nylon 66 | Edgetek™ |
| OmniLon鈩?PA6/6 HSL | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |