POLYelast TPE HJ752

Category: PP+EPDM , Polypropylene + EPDM Rubber
Manufacturer: Polykemi AB
Trademark: POLYelast
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: ZDaWeT_POLYelast-TPE-HJ752.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
PP/Elastomer Mineral reinforced
General Information
Filler / Reinforcement
  • Mineral, 15% Filler by Weight
PhysicalNominal ValueUnitTest Method
Density 0.980g/cm³ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)25g/10 minISO 1133
Molding Shrinkage ISO 294-4
    Across Flow 0.80 to 1.0%
    Flow 0.80 to 1.0%
MechanicalNominal ValueUnitTest Method
Tensile Stress 22.0MPaISO 527-2
Tensile Strain ISO 527-2
    Yield 9.0%
    Break 170%
Flexural Modulus (23°C)1700MPaISO 178
Flexural Stress 32.0MPaISO 178
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength ISO 179
    -20°C 5.0kJ/m²
    23°C 23kJ/m²
Charpy Unnotched Impact Strength ISO 179
    -20°C No Break
    23°C No Break
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature 1
    0.45 MPa, Unannealed 100°CISO 75-2/B
    1.8 MPa, Unannealed 57.0°CISO 75-2/A
Vicat Softening Temperature
    -- 130°CISO 306/A50
    -- 53.0°CISO 306/B50
CLTE - Flow 5.5E-5 to 6.5E-5cm/cm/°CInternal Method
Note Message
1 .120°C/hr
Resin Grade Manufacturer Category Trademark
Quadrant EPP PSU 1000 Quadrant Engineering Plastic Products PSU Quadrant EPP
Royalite R60-LS Spartech Plastics PMMA+PVC Royalite
NORYL™ 731 resin SABIC Innovative Plastics PPE+PS NORYL™
Mafill® CR CT 5544 H Ravago Group PP Copolymer Mafill®
Sylvin 8200-70 White 1452 Sylvin Technologies Incorporated PVC, Unspecified Sylvin