MXSTEN® DA77535
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | MXSTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZDA8Gq_MXSTEN-DA77535.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MXSTEN® DA77535 resin is a polyethylene plastomer designed for blown and cast film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness and higher melting point. Application/Uses: Blown film Cast film Stretch Film Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.914 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 172 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| TD : Yield, 25 µm, blown film | 6.69 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 35.2 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1200 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 400 | g | ASTM D1709A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, blown film | 300 | g | ASTM D1922 |
| TD : 25 µm, blown film | 550 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Sealing Initial Temperature 6 | 88 | °C | Internal method |
| Extrusion conditions used include a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 400° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| 6 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP 6D83G | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Kingfa PA6-RG30 | Kingfa | Nylon 6 | Kingfa |
| LUVOCOM® 20/SCF/30 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Hostacom TRC 2019N C12616 | LyondellBasell Industries | PP Copolymer | Hostacom |
| MARPOL® LL4M 812 | Marco Polo International, Inc. | LLDPE | MARPOL® |