Petro Rabigh PE FS253S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZCr3KD_Petro-Rabigh-PE-FS253S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FS253S is a linear low density polyethylene resin designed for blown film applications. This resin has a relatively high MFR that makes it an easy processing material. Films made from this resin exhibits high transparency, good toughness and good extrusion characteristics. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.080 | ||
| vs. Itself - Static | 0.11 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm | 205 | MPa | |
| 1% Secant, TD : 30 µm | 250 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 35.0 | MPa | |
| TD : Break, 30 µm | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 770 | % | |
| TD : Break, 30 µm | 930 | % | |
| Dart Drop Impact (30 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 130 | g | |
| TD : 30 µm | 350 | g | |
| Blocking Load | 14 | g | ASTM D3354 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm) | 55 | ASTM D2457 | |
| Haze (30.0 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4803 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NEXUS Reprocessed PPC 20/10 RBK | Nexus Resin Group, LLC. | PP Copolymer | NEXUS Reprocessed |
| FHR EPS 54-S7354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Pacrel® 5365N-NA | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Moplen EP500N | PolyMirae | PP Impact Copolymer | Moplen |