Lumid® HI5063A(W)
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZB8nag_Lumid-HI5063A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact Application Electric/Electronic Components(Shaver Die) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 46.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 60 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1960 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 90.0 | °C | ASTM D648 |
| CLTE - Flow | 6.5E-5 to 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 245 to 260 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 260 to 275 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure 5 | 0.981 to 2.94 | MPa | |
| Screw Speed | 60 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Skyrol® SP91 | SKC Inc. | PET | Skyrol® |
| Niuk 20NT01 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| Karina COKE PVC COMPOUND 830-21/9-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrotene® PP A3 T35 PRTA011 PH355 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Durethan® BKV 25 F30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |