Tenac™-C EF750
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZArQNn_Tenac--C-EF750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C EF750 is an Acetal (POM) Copolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C EF750 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.6 to 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 52.0 | MPa | ISO 527-2 |
| -- | 48.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2450 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Strength | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 162 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| -- | 1.0E-4 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| -- | 10 to 1.0E+2 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+2 to 1.0E+4 | ohms·cm | ASTM D257 |
| -- | 10 to 1.0E+2 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 863 | RTP Company | Acetal (POM) Copolymer | RTP |
| Fainplast PVC PH 61/K1-AM | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Huafon JF-S-H8021 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Capilene® G 78 TF | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Hostacom ERC 2061N | LyondellBasell Industries | PP, Unspecified | Hostacom |