RTP 6001-50A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZAP8h9_RTP-6001-50A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RTP 6001-50A is a Thermoplastic Elastomer (TPE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 0.896 | MPa | ASTM D412 |
| Tensile Strength 2(Yield, 3.20 mm) | 5.86 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 930 | % | ASTM D412 |
| Tear Strength 4 | 22.8 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 15 | % | |
| 70°C, 22 hr | 65 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 51.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 182 to 238 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C |
| Note Message | |
|---|---|
| 1 . | Die C, 510 mm/min |
| 2 . | Die C, 500 mm/min |
| 3 . | Die C, 500 mm/min |
| 4 . | Die C |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| TAISOX 7350F | Formosa Plastics Corporation | EVA | TAISOX |
| ADENE ACJB | A.D. Compound spa | PP Homopolymer | ADENE |
| Hypro-G™ PP-HP12 | Entec Polymers | PP Homopolymer | Hypro-G™ |
| Kepamid® 1900SF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |