Lustran® ABS LGM
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z9bKOO_Lustran-ABS-LGM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS LGM is a low-gloss, easy-flow grade of ABS (Acrylonitrile Butadiene Styrene). This general-purpose injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance. Lustran ABS LGM resin is designed for applications requiring stringent physical properties and a high-tech, low-gloss appearance. Typical applications include power tool housings; lawn and garden equipment; telecommunications equipment; and business machine applications, such as keyboard housings, keypads, and keycaps. As with any product, use of Lustran ABS LGM resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 21 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 35.9 | MPa | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 88.9 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 92.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 100 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 75.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 1 |
| CLTE - Flow (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI (1.57 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.57 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 266 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 - 75% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 1200GF | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Daelim Po1y® PP-172 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| MAJORIS DFR101 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 2960-80 White 1500 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Durethan® BKV 215 H2.0 DUS035 900051 | LANXESS GmbH | Nylon 6 | Durethan® |