NORYL™ FXN4020H resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z98bzW_NORYLFXN4020Hresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| high gloss NORYL |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.060 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 9.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2560 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 67.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 46.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.6 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/50 |
| Fracture 5 | 5.2 | % | ASTM D638 |
| Fracture | 4.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2730 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 85.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 20 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 10 | 4.6 | kJ/m² | ISO 180/1A |
| 23°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 98.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-1 | UL 94 | |
| 2.50 mm, Testing by SABIC | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 216 - 266 | °C | |
| Middle Temperature | 227 - 271 | °C | |
| Front Temperature | 238 - 277 | °C | |
| Nozzle Temperature | 249 - 277 | °C | |
| Processing (Melt) Temp | 249 - 277 | °C | |
| Mold Temperature | 54.4 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2021GR | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Shandong Aobang TPU-Polyester 80-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| VESTAMID® L L1930 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| NEXT REGRIND PC/ABS 830-300RG | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REGRIND |
| ALTECH® PA66 A 2040/100 GF40 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |