Desmopan® DP 3072D
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z8yNhY_Desmopan-DP-3072D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; high mechanical strength; excellent abrasion resistance; good wear resistance; very short cycle times; Application; Technical parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 98 | ||
| Shore D, 23°C | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 60.0 | MPa | |
| 100% Strain, 23°C | 34.0 | MPa | |
| 300% Strain, 23°C | 52.0 | MPa | |
| Tensile Strain 2(Break, 23°C) | 350 | % | DIN 53504 |
| Flexural Modulus 3(23°C) | 800 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 20.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 3.33 | GPa | |
| 20°C | 1.28 | GPa | |
| 60°C | 0.385 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 47 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4(23°C) | 260 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 29 | % | |
| 70°C, 24 hr | 49 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 225 to 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 22LHI4 XE-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| TRIEL® 5550 | Samyang Corporation | TPEE | TRIEL® |
| GAPEX® RPP30DA13NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| INEOS PP H28E-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| LNP™ VERTON™ RV008ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |