Nycal™ 1850N6/X
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z8sCXZ_Nycal-1850N6-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nycal™ 1850N6/X is a Polyamide 6 (Nylon 6) material. It is available in North America for injection molding. Important attributes of Nycal™ 1850N6/X are:
Typical application of Nycal™ 1850N6/X: Plumbing/Piping/Potable Water |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 15 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 280 | °C | |
| Mold Temperature | 40.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 to 0.689 | MPa | |
| Screw Speed | 100 | rpm | |
| Clamp Tonnage | 3.4 to 5.5 | kN/cm² | |
| Cushion | 6.35 to 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VET30C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Unichem 9613 | Colorite Polymers | PVC, Flexible | Unichem |
| LNP™ FARADEX™ AS004 compound | SABIC Innovative Plastics Europe | ABS | LNP™ FARADEX™ |
| Hostacom EKC 330N NA DS2 Granitgra | LyondellBasell Industries | TPO (POE) | Hostacom |
| 3M™ Dyneon™ PTFE Compound TF 6712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |