DENKA ABS GR-2000LG
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z8hp6M_DENKA-ABS-GR-2000LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA ABS GR-2000LG is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 | g/cm³ | ASTM D792 |
| 23°C | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 35.0 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 37.0 | MPa | |
| Break | 29.0 | MPa | |
| Nominal Tensile Strain at Break | 51 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1900 | MPa | ASTM D790 |
| -- 3 | 1950 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 57.0 | MPa | ASTM D790 |
| -- 5 | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 32 | kJ/m² | ISO 179 |
| Notched Izod Impact | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 7 |
| -- | 97.0 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | > 1.0E+16 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 210 to 260 | °C | |
| Nozzle Temperature | 210 to 255 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| 8 . | 23°C, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-GP1-(color)H | Polymer Resources Ltd. | Nylon 66 | PRL |
| SABIC® LDPE 2200H2 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Pyramid™ PEEK KD2540-NT | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Catalyst CT 0552/09 | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Sylvin 8250-90 Grey 9530 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |