Petra® 230 BK-112
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z8h4Bk_Petra-230-BK-112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties including high strength and stiffness with ductility at elevated temperatures, good chemical resistance, dimensional stability and warp resistance. Applications Petra 230 BK-112 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -40°C | 12300 | MPa | |
| 23°C | 11700 | MPa | |
| 80°C | 4120 | MPa | |
| 121°C | 2590 | MPa | |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Break, -40°C | 145 | MPa | |
| Break, 23°C | 115 | MPa | |
| Break, 80°C | 60.0 | MPa | |
| Break, 121°C | 45.0 | MPa | |
| Tensile Elongation | |||
| Break, -40°C | 1.6 | % | ASTM D638 |
| Break, 23°C | 2.0 | % | ASTM D638, ISO 527-2 |
| Break, 80°C | 6.3 | % | ASTM D638 |
| Break, 121°C | 8.1 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 9050 | MPa | ASTM D790 |
| 23°C | 8760 | MPa | ISO 178 |
| Flexural Strength (23°C) | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 55 | J/m | ASTM D256 |
| 23°C | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 206 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Peak Melting Temperature | 245 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX GFR 5 | Taro Plast S.p.A. | PBT | TAROLOX |
| Tarnamid® T-27 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Globalprene® 3710 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| SABIC® FORTIFY™ C0560D | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |
| Sylvin 8707-84 Grey 9478 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |