LNP™ LUBRICOMP™ RX05495 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z7gXRO_LNP-LUBRICOMP-RX05495-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing 30% Glass Bead, Graphite, Glass Fiber, 5% Graphite Powder. Added features of this material include: Easy Molding. Heat Stabilized, Mold Release, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4316 EM HS MG MR Product reorder name: RX05495 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.5 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.46 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.84 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8000 | MPa | ASTM D638 |
| -- | 7500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 118 | MPa | ASTM D638 |
| Break | 113 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.8 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6140 | MPa | ASTM D790 |
| -- | 7100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 174 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 670 | J/m | ASTM D4812 |
| 23°C 3 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.6 | J | ASTM D3763 |
| -- | 2.32 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 256 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 234 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 229 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ OLS100 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| VITAMIDE® AF30BK6030 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Elvacite® 2016 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| StarMed® 9015-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMed® |
| LNP™ COLORCOMP™ D1000P compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |