Ferro PP TPP40AC45BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z7KBDv_Ferro-PP-TPP40AC45BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Meets/Exceeds Ford Engineering Specification ESA-M4D166-A. Primary end use is for fan shrouds and battery covers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 31.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3800 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 52.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 131 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 210 | °C | |
| Middle Temperature | 210 to 213 | °C | |
| Front Temperature | 213 to 216 | °C | |
| Nozzle Temperature | 216 to 218 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF6FMA (Series: FC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Celstran® PA66-SF50-02 AF3001 | Celanese Corporation | Nylon 66 | Celstran® |
| ELASTOSIL® E 43 N | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Escorene™ Ultra UL 7760 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| PARAPET GR-H60 | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |