Witcom ABS AS is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 to 0.90 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 30 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | > 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 to 1.0E+11 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6050 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| UNITIKA Nylon 6 A1030GFL | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| New-prene™ 9150N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| LG ABS EF378L | LG Chem Ltd. | ABS | LG ABS |
| Plasmer 5040DN/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |