DENKA Transparent Polymer TE-30S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z6kxVT_DENKA-Transparent-Polymer-TE-30S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA Transparent Polymer TE-30S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/5.0 kg | 1.2 | g/10 min | |
| 220°C/10.0 kg | 19 | g/10 min | |
| Molding Shrinkage (2.00 mm) | 0.50 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 37 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 28 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1700 | MPa | ISO 178 |
| Flexural Stress 2 | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 17 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 84.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 91.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 1.8 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evoprene™ COGEE 634 | AlphaGary | SEBS | Evoprene™ COGEE |
| Evoprene™ 029 | AlphaGary | SBS | Evoprene™ |
| Generic Epoxy - Glass Fiber | Generic | Epoxy | Generic |
| LUVOCOM® 65-9048/L | LEHVOSS Group | PP Copolymer | LUVOCOM® |
| Rotuba CAB B9024 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |