Generic Nylon 612
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z6c5al_Generic-Nylon-612.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 612 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.35 | g/cm³ | ASTM D792 |
| 23°C | 1.06 - 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.23 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 2.0 | % | ASTM D955 |
| 23°C | 1.1 - 1.8 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.13 - 0.38 | % | ASTM D570 |
| Saturated, 23°C | 3.0 - 4.0 | % | ASTM D570 |
| Saturated, 23°C | 2.1 - 3.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.88 - 1.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 108 - 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1650 - 2540 | MPa | ASTM D638 |
| 23°C | 275 - 7950 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 45.0 - 65.0 | MPa | ASTM D638 |
| Yield, 23°C | 48.6 - 62.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 30.0 - 141 | MPa | ISO 527-2 |
| 23°C | 31.4 - 173 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 3.2 - 40 | % | ASTM D638 |
| Yield, 23°C | 4.0 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 2.5 - 300 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 55 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 17 - 300 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1770 - 8640 | MPa | ASTM D790 |
| 23°C | 1300 - 2110 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 23.0 - 296 | MPa | ASTM D790 |
| 23°C | 28.5 - 71.1 | MPa | ISO 178 |
| Coefficient of Friction | 0.13 - 1.0 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 96 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 36 - 81 | J/m | ASTM D256 |
| 23°C | 3.7 - 5.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 560 - 1300 | J/m | ASTM D256 |
| Tensile Impact Strength (23°C) | 126 - 945 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 132 - 212 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 134 - 172 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.1 - 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.7 - 75.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 108 - 201 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 208 - 215 | °C | |
| -- | 215 - 218 | °C | ISO 11357-3 |
| -- | 200 - 211 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 4.9E-5 - 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 8.6E-5 - 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.0E-5 - 1.8E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 55 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+10 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 22 - 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.48 - 6.00 | ASTM D150 | |
| 23°C | 4.14 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.017 - 0.15 | ASTM D150 | |
| 23°C | 0.014 - 0.15 | IEC 60250 | |
| Comparative Tracking Index | 598 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 719 - 725 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 700 - 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 2.9 - 4.1 | hr | |
| Suggested Max Moisture | 0.060 - 0.25 | % | |
| Rear Temperature | 227 - 269 | °C | |
| Middle Temperature | 229 - 268 | °C | |
| Front Temperature | 227 - 277 | °C | |
| Nozzle Temperature | 232 - 258 | °C | |
| Processing (Melt) Temp | 253 - 275 | °C | |
| Mold Temperature | 69.4 - 79.8 | °C | |
| Injection Pressure | 96.3 - 98.7 | MPa | |
| Back Pressure | 0.250 - 0.689 | MPa | |
| Screw Speed | 45 - 100 | rpm | |
| Cushion | 3.97 - 7.94 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 612This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.060 - 0.061 | % |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 612This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V897 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Varcum 29461 | Durez Corporation | Phenolic | Varcum |
| Electrafil® PA6 CF20 BK | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Karina ORANGE COLOR CONCENTRATE -E 32/ 76-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Silastic® Q7-4750 | Dow Corning Corporation | Silicone | Silastic® |