BESTPOLUX PCTM
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z6IIvL_BESTPOLUX-PCTM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/PETnatural lubrified with impact modified to gain improvements in injection and moulding generally used for pieces in conjunction with improved dimesional stability, better impact and good final surface for general industry. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 30 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 54 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Dielectric Strength | 35 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Humidity Pellets, ISO 1110: 0.2%Flammability Speed, FMV 302:<100 mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 275 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1035 04 F | ROMIRA GmbH | PC+ABS | Romiloy® |
| Sindustris PP GP3203Z | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 86010-85FUV Clear Black 286 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| INEOS Wire & Cable BPD4035 | INEOS Olefins & Polymers Europe | MDPE | INEOS Wire & Cable |
| Karina COMP. PVC IVORY -E 853-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |