Generic PC
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z5gKCe_Generic-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 - 1.22 | g/cm³ | ASTM D792 |
| 23°C | 1.20 - 1.23 | g/cm³ | ISO 1183 |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| -- | 1.19 - 1.20 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.64 - 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 300°C/1.2 kg | 1.8 - 26 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 1.0 - 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 300°C/1.2 kg | 4.38 - 24.6 | cm³/10min | ISO 1133 |
| -- | 11.6 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.53 - 0.70 | % | ASTM D955 |
| Transverse flow : 23°C | 0.57 - 0.72 | % | ASTM D955 |
| 23°C | 0.46 - 0.76 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.15 - 0.21 | % | ASTM D570, ISO 62 |
| Saturated, 23°C | 0.34 - 0.35 | % | ASTM D570 |
| Saturated, 23°C | 0.30 - 0.35 | % | ISO 62 |
| Equilibrium, 23°C | 0.32 - 0.35 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.066 - 0.18 | % | ISO 62 |
| Viscosity Number | 45.9 - 50.1 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 69 - 121 | ASTM D785 | |
| 23°C | 50 - 121 | ISO 2039-2 | |
| Ball Indentation Hardness | 94.0 - 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2140 - 2670 | MPa | ASTM D638 |
| 23°C | 2030 - 2430 | MPa | ISO 527-2 |
| -- | 2300 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, 23°C | 56.0 - 64.4 | MPa | ASTM D638 |
| Yield, 23°C | 56.2 - 66.8 | MPa | ISO 527-2 |
| Yield | 60.1 | MPa | ISO 527-2 4 |
| Fracture, 23°C | 50.4 - 73.8 | MPa | ASTM D638 |
| Fracture, 23°C | 48.9 - 77.2 | MPa | ISO 527-2 |
| 23°C | 57.0 - 67.6 | MPa | ASTM D638 |
| 23°C | 59.6 - 60.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.9 - 7.4 | % | ASTM D638 |
| Yield, 23°C | 5.5 - 7.0 | % | ISO 527-2 |
| Yield | 6.0 | % | ISO 527-2 5 |
| Fracture, 23°C | 0.0 - 140 | % | ASTM D638 |
| Fracture, 23°C | 46 - 150 | % | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 75 - 150 | % | ASTM D1708 |
| Nominal Tensile Strain at Break (23°C) | 50 - 53 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2200 | MPa | ISO 899-1 |
| 1000 hr | 1880 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 1730 - 2880 | MPa | ASTM D790 |
| 23°C | 2090 - 2470 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 80.1 - 110 | MPa | ASTM D790 |
| 23°C | 89.8 - 98.5 | MPa | ISO 178 |
| Yield, 23°C | 83.6 - 104 | MPa | ASTM D790 |
| Fracture, 23°C | 80.5 - 96.2 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 62.1 - 86.2 | MPa | ASTM D695 |
| Coefficient of Friction | 0.060 - 0.39 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 9.90 - 10.8 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 7.1 - 80 | kJ/m² | ISO 179 |
| -30°C | 13.1 | kJ/m² | ISO 179/1eA 6 |
| 23°C | 61.9 | kJ/m² | ISO 179/1eA 7 |
| Charpy Unnotched Impact Strength (23°C) | 10 - 300 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 61 - 940 | J/m | ASTM D256 |
| 23°C | 7.6 - 83 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 11.0 - 60.4 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 3100 - 3300 | J/m | ASTM D256 |
| 23°C | 22 - 190 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 54.9 - 102 | J | ASTM D3763 |
| 23°C | 48.3 - 63.6 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 4850 - 5610 | N | ISO 6603-2 |
| Dart Drop Impact (23°C) | 35.1 - 170 | J | ASTM D3029 |
| Tensile Impact Strength (23°C) | 375 - 641 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 130 - 141 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 130 - 142 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 139 - 146 | °C | ASTM D648 |
| 0.45 MPa, annealed | 136 - 146 | °C | ISO 75-2/B |
| 0.45 MPa | 143 | °C | ISO 75-2 8 |
| 1.8 MPa, not annealed | 121 - 139 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 114 - 131 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 136 - 143 | °C | ASTM D648 |
| 1.8 MPa, annealed | 122 - 143 | °C | ISO 75-2/A |
| 1.8 MPa | 130 | °C | ISO 75-2 9 |
| Continuous Use Temperature | 120 - 132 | °C | ASTM D794 |
| Glass Transition Temperature | |||
| -- | 143 - 146 | °C | ISO 11357-2 |
| -- | 145 - 149 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 136 - 155 | °C | ASTM D1525 |
| -- | 135 - 151 | °C | ISO 306 |
| 50°C/h, B (50N) | 149 | °C | ISO 306 10 |
| Ball Indentation Temperature | 125 | °C | IEC 60598-1 |
| Melting Temperature | 224 - 252 | °C | |
| Linear thermal expansion coefficient | |||
| Flow | 5.8E-5 - 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flow | 6.5E-5 - 7.1E-5 | cm/cm/°C | ASTM E831 |
| Flow | 6.4E-5 - 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 11 |
| Lateral | 3.6E-5 - 2.1E-4 | cm/cm/°C | ASTM D696 |
| Lateral | 5.9E-5 - 8.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 6.0E-5 - 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1250 - 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| 23°C | 0.15 - 0.40 | W/m/K | ASTM C177 |
| 23°C | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 77.5 - 130 | °C | UL 746 |
| RTI Imp | 80.0 - 130 | °C | UL 746 |
| RTI | 77.5 - 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 10 - 2.8E+15 | ohms | ASTM D257 |
| -- | 6.0 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 10 - 1.5E+17 | ohms·cm | ASTM D257 |
| 23°C | 0.50 - 2.0E+19 | ohms·cm | IEC 60093 |
| -- | 1.0E+13 - 1.2E+13 | ohms·m | IEC 60093 12 |
| Dielectric Strength | |||
| 23°C | 15 - 30 | kV/mm | ASTM D149 |
| 23°C | 17 - 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.84 - 3.17 | ASTM D150 | |
| 23°C | 2.70 - 3.26 | IEC 60250 | |
| 23°C | 2.90 | IEC 60250 | |
| 100 Hz | 3.00 | IEC 60250 13 | |
| Dissipation Factor (23°C) | 4.0E-4 - 0.010 | ASTM D150, IEC 60250 | |
| Arc Resistance | 110 - 120 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 300 - 301 | V | UL 746 |
| Comparative Tracking Index | 119 - 256 | V | IEC 60112 |
| Insulation Resistance (23°C) | 9.8E+11 - 1.0E+12 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 2.5 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 850 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 772 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 25 - 35 | % | ASTM D2863 |
| -- | 25 - 40 | % | ISO 4589-2 |
| -- | 26 | % | ISO 4589-2 14 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | |||
| -- | 1.584 - 1.586 | ASTM D542 | |
| -- | 1.586 | ISO 489 | |
| Transmittance | 86.5 - 91.0 | % | ASTM D1003 |
| Haze | 0.20 - 2.7 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 122 | °C | |
| Drying Time | 2.9 - 5.2 | hr | |
| Drying Time, Maximum | 47 | hr | |
| Dew Point | -29.0 - -28.6 | °C | |
| Suggested Max Moisture | 0.015 - 0.040 | % | |
| Suggested Shot Size | 50 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 66.2 - 71.6 | °C | |
| Rear Temperature | 253 - 304 | °C | |
| Middle Temperature | 260 - 310 | °C | |
| Front Temperature | 274 - 322 | °C | |
| Nozzle Temperature | 269 - 302 | °C | |
| Processing (Melt) Temp | 280 - 305 | °C | |
| Mold Temperature | 80.1 - 101 | °C | |
| Injection Pressure | 84.9 - 101 | MPa | |
| Holding Pressure | 5.17 - 90.0 | MPa | |
| Back Pressure | 0.412 - 0.599 | MPa | |
| Screw Speed | 55 - 62 | rpm | |
| Clamp Tonnage | 4.8 - 6.1 | kN/cm² | |
| Cushion | 4.76 - 6.43 | mm | |
| Vent Depth | 0.050 - 0.063 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PCThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 124 | °C | |
| Drying Time | 2.8 - 13 | hr | |
| Hopper Temperature | 50.0 - 110 | °C | |
| Cylinder Zone 1 Temp. | 166 - 278 | °C | |
| Cylinder Zone 2 Temp. | 171 - 321 | °C | |
| Cylinder Zone 3 Temp. | 177 - 332 | °C | |
| Cylinder Zone 4 Temp. | 182 - 277 | °C | |
| Cylinder Zone 5 Temp. | 267 - 275 | °C | |
| Adapter Temperature | 240 - 275 | °C | |
| Melt Temperature | 191 - 277 | °C | |
| Die Temperature | 98.9 - 275 | °C | |
| Calibration Temp, First | 75.0 - 80.3 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PCThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 977-S | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| MOSTEN GB 503 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| Hostacom 6652 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Jampilen ADXP680 | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| PENTAMID A GV40 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |