SABIC® PPcompound 1920
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z5XoNU_SABIC-PPcompound-1920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 1920 is an FDA compliant, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. The IMDS ID is 482238095 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 23°C, 48 hr | 1.3 | % | |
| Flow : 23°C, 48 hr | 0.95 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2970 | MPa | ASTM D638 |
| -- | 3210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 36.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Break 3 | 29.0 | MPa | ASTM D638 |
| Break | 32.7 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Break 5 | 21 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 64.0 mm Span 6 | 3180 | MPa | ISO 178 |
| 50.0 mm Span 7 | 2500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 1.1 | kJ/m² | |
| 23°C 9 | 2.5 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 10 | 22 | J/m | ASTM D256 |
| -30°C 11 | 1.3 | kJ/m² | ISO 180/1A |
| 23°C 12 | 2.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 13(23°C, 3.20 mm) | 410 | J/m | ASTM D4812 |
| Instrumented Dart Impact 14(23°C, Energy at Peak Load) | 3.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 15 | 128 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 73.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 16 | 73.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 58.3 | µm/Mk | |
| Transverse : -30 to 100°C | 115 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 63.5*12.7*3.2mm, Cut |
| 11 . | 80*10*4mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 63.5*12.7*3.2mm, Cut |
| 14 . | 2.20 m/sec |
| 15 . | 80*10*4mm, Cut |
| 16 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 HF UV | RTP Company | PC | RTP |
| VESTAMID® L L2121 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Toyolac® 450Y X10 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Ferro PP NPP00GT22BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Lucolit® 1310 | Lucobit AG | TPO (POE) | Lucolit® |