Macromeric® 0110-108 BK
| Category: | CPE , Chlorinated Polyethylene |
| Manufacturer: | Saco Polymers |
| Trademark: | Macromeric® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z4t8ba_Macromeric-0110-108-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lead-free Thermoplastic CPE compound Macromeric ® 0110-108 BK is a black, UV resistant, Lead-free, RoHS compliant, Thermoplastic CPE compound. It is designed for use in a wide variety of jacketing applications including wire and cable and tube bundles. This compound has superior fire performance; including slow flame propagation, and self-extinguishing characteristics. Macromeric ® 0101-108 BK should be extruded with a screw configuration designed to optimize process conditions and throughput. This extrusion compound is designed to meet the jacketing requirements of commonly cited cable specifications, including UL 1277 tray cable. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec | 91 | ||
| Shore D, 10 sec | 52 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 345 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 78.8 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (121°C, 168 hr) | -5.0 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (121°C, 168 hr) | -15 | % | ASTM D638 |
| Change in Tensile Strength | ASTM D638 | ||
| 75°C, 1440 hr, in IRM 902 Oil | -20 | % | |
| 100°C, 96 hr, in IRM 902 Oil | -25 | % | |
| Change in Ultimate Elongation | ASTM D638 | ||
| 75°C, 1440 hr, in IRM 902 Oil | -25 | % | |
| 100°C, 96 hr, in IRM 902 Oil | -25 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 2 | -33.0 | °C | ASTM D746 |
| Deformation - 2000-gram load | UL 1277 | ||
| 100°C | 7.0 | % | |
| 121°C | 14 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 174 to 185 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index 3 | 44 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 to 160 | °C | |
| Cylinder Zone 2 Temp. | 160 to 174 | °C | |
| Cylinder Zone 3 Temp. | 174 to 185 | °C | |
| Cylinder Zone 4 Temp. | 174 to 185 | °C | |
| Melt Temperature | 174 to 185 | °C | |
| Die Temperature | 174 to 185 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 3 minutes in methanol |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B6246 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Sasol Polymers PP HRV100 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Ecomass® 3620BX60 | Ecomass Technologies | HDPE | Ecomass® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| Plaslube® PPS-1305/TF/20/NAT | Techmer Engineered Solutions | PPS | Plaslube® |