LEXAN™ HF3454 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z497p3_LEXAN-HF3454-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GF filled, Non-brominated/non-chlorinated FR PC. High flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 22.0 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4000 | MPa | ASTM D638 |
| -- | 4000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Break 3 | 40.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.1 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5 |
| Break 5 | 6.9 | % | ASTM D638 |
| Break | 6.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3600 | MPa | ASTM D790 |
| -- 7 | 4000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 108 | MPa | ISO 178 |
| -- | 110 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 104 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 42 | J/m | ASTM D256 |
| 23°C | 45 | J/m | ASTM D256 |
| -30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| -30°C 11 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 14 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 15.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 113 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 121 | °C | ASTM D1525 16 |
| -- | 124 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 260 to 277 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 271 to 299 | °C | |
| Nozzle Temperature | 271 to 299 | °C | |
| Processing (Melt) Temp | 271 to 310 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 35 to 75 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 |
| 12 . | 80*10*3 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 107 | RTP Company | PP, Unspecified | RTP |
| Etinox® EI-6420 | Ercros, S.A. | PVC, Flexible | Etinox® |
| Geon™ Vinyl Rigid Extrusion 87717 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| LOXIM 330 01 V0 | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| MAXAMID™ EPDMRC0366-HSL-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |