NORYL™ WCV063 resin
| Category: | PPE+SEBS+Polyolefin , Polyphenylene Ether + SEBS + Polyolefin |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z44Zpu_NORYL-WCV063-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 33 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 840 | MPa | ASTM D638 |
| -- | 690 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 28.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2 |
| Fracture 3 | 28.0 | MPa | ASTM D638 |
| Fracture | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 20 | % | ISO 527-2/50 |
| Fracture 4 | 90 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 5 | 720 | MPa | ASTM D790 |
| -- | 790 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 170 | J/m | ASTM D256 |
| 23°C | 560 | J/m | ASTM D256 |
| -30°C 6 | 14 | kJ/m² | ISO 180/1A |
| 23°C 7 | 37 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 56.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 8 | 66.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 2.47 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 3.2E-3 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 200 - 260 | °C | |
| Cylinder Zone 3 Temp. | 270 - 300 | °C | |
| Cylinder Zone 5 Temp. | 280 - 300 | °C | |
| Melt Temperature | 280 - 300 | °C | |
| Die Temperature | 280 - 300 | °C |
| Extrusion instructions |
|---|
| Compression Ratio 2;1-3:1Conductor Pre-heat Temperature: 100 - 150 °CCooling Water Air Gap: 100 - 1000 mmCross-head Temperature: 280 - 300 °CDrying Time (Cumulative): 8 hrsExtruder Length/Diameter Ratio (L/D): >24:1Neck Temperature: 280 - 300 °CScreen Pack: 60/200/60Screw Speed: 5 - 60 rpmWater Bath Temperature: 15 - 30 °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 74-8126A-22 | Teknor Apex Company | PVC, Flexible | APEX® |
| Europrene® NEOCIS BR 60 | Versalis S.p.A. | PBR, High Cis | Europrene® |
| EVAL™ G156B | EVAL Europe nv | EVOH | EVAL™ |
| ELIX™ ABS P2M-V | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Iupilon® GSH2030SR 9920A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |