Kepital® F20-52G
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z3Klme_KepitalF2052G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An easy-flowing grade for general injection molding. It's modified with a weather-resistant and gloss-reducing substance, and so suitable for parts requiring a good weather resistance and low gloss characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 58.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ASA E 210 | ROMIRA GmbH | ASA | Rotec® ASA |
| YUNGSOX® PP 3204 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| VALOX™ 7062HP resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| DURANEX® C5315N | Polyplastics Co., Ltd. | PBT+PET | DURANEX® |
| LONGLITE® PMC T391 | CCP Group | Phenolic | LONGLITE® PMC |