Honeywell PCTFE P5000HS

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Z37qVG_Honeywell-PCTFE-P5000HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Honeywell PCTFE P-Series HS film is a copolymer poly-chlor-tri-fluoroethylene film. Honeywell PCTFE HS film has the ability to heat seal to itself utilizing impulse sealing methods.

General Information
Features	Copolymer Heat sealable
Uses	Films
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.08	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1380	MPa	ASTM D882
TD	1280	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	48.3	MPa	ASTM D882
TD : Fracture	34.5	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	200	%	ASTM D882
TD : Fracture	200	%	ASTM D882
Water Vapor Transmission	0.093	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	190	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 1.0	%	ASTM D1003

Additional Information
Yield: 2659 in²/lbTensile Strength @ Break, ASTM D 882, MD: 6000 to 8000 psiTensile Strength @ Break, ASTM D 882, TD: 4000 to 6000 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 150 to 250%Secant Modulus, ASTM D 882, MD: 180000 to 220000 psiSecant Modulus, ASTM D 882, TD: 170000 to 200000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 300 to 350 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <3% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <3% shrinkageFlammability: Non-flammable

Additional Information

Yield: 2659 in²/lbTensile Strength @ Break, ASTM D 882, MD: 6000 to 8000 psiTensile Strength @ Break, ASTM D 882, TD: 4000 to 6000 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 150 to 250%Secant Modulus, ASTM D 882, MD: 180000 to 220000 psiSecant Modulus, ASTM D 882, TD: 170000 to 200000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 300 to 350 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <3% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <3% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
Radiflam® S AEK 121 C NAT 4293	Radici Plastics	Nylon 6	Radiflam®
SITRADUR 35E / C01000	SITRAPLAS GmbH	PBT	SITRADUR
XYRON™ 600H	Asahi Kasei Chemicals Corporation	PPE+PS	XYRON™
AKROMID® A3 GF 40 1 L black (4671)	AKRO-PLASTIC GmbH	Nylon 66+PP	AKROMID®
Hanwha Total PE 310A	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	LDPE	Hanwha Total PE