EPLON 66 GFR 30 BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLON 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z2h3Lx_EPLON-66-GFR-30-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This product is available in black and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.33 - 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 3.00mm | 0.70 | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.50 | % | ISO 294-4 |
| Moisture Content | 0.20 | % | ISO 15512 |
| Ash Content | 28 - 32 | % | ISO 3451-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 84 - 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7500 - 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 - 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6500 - 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 - 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 - 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 240 - 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP111 | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| Nanjing Hongrui PBT T304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Cheng Yu IPS600UV | Cheng Yu Plastic Company Limited | PS (HIPS) | Cheng Yu |
| KEBAFORM® C 904 GB | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LNP™ THERMOCOMP™ LC004XXP compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |