Arlon® 3000 XT
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z2YpyV_Arlon-3000-XT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arlon® 3000 XT is a Polyetheretherketone (PEEK) product. It can be processed by injection molding and is available in Europe or North America. Primary characteristic: heat resistant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| 24°C | 3930 | MPa | |
| 200°C | 1330 | MPa | |
| 260°C | 654 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 24°C | 112 | MPa | |
| Yield, 200°C | 40.0 | MPa | |
| Yield, 260°C | 28.3 | MPa | |
| Break, 24°C | 121 | MPa | |
| Break, 200°C | 59.4 | MPa | |
| Break, 260°C | 38.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Break, 24°C | 15 | % | |
| Break, 200°C | > 25 | % | |
| Break, 260°C | > 25 | % | |
| Flexural Modulus | ASTM D790 | ||
| 24°C | 4410 | MPa | |
| 200°C | 1800 | MPa | |
| 260°C | 827 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 5.0% Strain, 24°C | 165 | MPa | |
| 5.0% Strain, 200°C | 61.0 | MPa | |
| 5.0% Strain, 260°C | 32.2 | MPa | |
| Compressive Modulus | ASTM D695 | ||
| -- 4 | 724 | MPa | |
| -- 5 | 1700 | MPa | |
| -- 6 | 3860 | MPa | |
| Compressive Strength | ASTM D695 | ||
| 260°C | 34.8 | MPa | |
| 200°C | 62.7 | MPa | |
| 24°C | 154 | MPa | |
| Shear Strength | ASTM D732 | ||
| 24°C | 111 | MPa | |
| 200°C | 65.2 | MPa | |
| 260°C | 48.6 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 300 | °C | ASTM D648 |
| Melting Temperature | 352 | °C | DSC |
| CLTE - Flow 7 | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.02 mm) | 29 | kV/mm | ASTM D149 |
| Dielectric Constant (1.02 mm, 1 MHz) | 1.96 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | Type I |
| 3 . | Type I |
| 4 . | 500°F |
| 5 . | 392°F |
| 6 . | 75°F |
| 7 . | T |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-GP5 | Polymer Resources Ltd. | PPE+PS | PRL |
| Reon 57GER01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| UBESTA 3020X29L | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Hanwha Total PP RP100W130 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Sylvin 9655-68 Clear 8384 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |