Plexiglas® Satinice df20 8N
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z2NOeU_Plexiglas-Satinice-df20-8N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLEXIGLAS® Satinice df20 8N based on PLEXIGLAS® 8N are characterized by diffuse scattering of light. Besides showing the familiar properties of standard PLEXIGLAS® molding compound, such as
PLEXIGLAS® Satinice df20 8N is special in that they combine
Application: Used for injection molding items for lighting engineering pplications Examples: displays, fiber optics, projection screens, lighting fixtures and similar applications in lighting engineering. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 2.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 74.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 108 | °C | ISO 306/B50 |
| CLTE - Flow (0 to 50°C) | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Fire Rating | B2 | DIN 4102 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half-Value Angle | 1.60 | ° | DIN 5036 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 1 | 88.0 | % | ISO 13468-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 95.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1100 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Tenac™-C HC460 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Generic PP Homopolymer - Glass Fiber, Long | Generic | PP Homopolymer | Generic |
| Generic PC - Unspecified | Generic | PC | Generic |
| LNP™ THERMOCOMP™ EX11414 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |