IROGRAN® A 92 P 4851
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z0pOUo_IROGRAN-A-92-P-4851.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 92 P 4851 is a thermoplastic polyether-polyurethane for injection moulding and extrusion applications. Additional characteristics of the product are high extrudability and low-adhesion surfaces. PERFORMANCE FEATURES
APPLICATIONS For the production of jacket material for cables, jackets for high pressure spiral hoses, profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.14 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 55.0 | cm³/10min | |
| Molding Shrinkage | |||
| Flow | 0.10 | % | ASTM D955 |
| -- | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, Injection Molded | 93 | ||
| Shore D, Injection Molded | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 35 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 10.0 | MPa | ASTM D412, DIN 53504 |
| 300% Strain | 14.5 | MPa | ASTM D412 |
| 300% Strain | 16.0 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 35.9 | MPa | ASTM D412 |
| Break | 40.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 630 | % | ASTM D412 |
| Break | 600 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 112 | kN/m | ASTM D624 |
| -- | 75 | kN/m | ISO 34-1 |
| Compression Set 7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 45 | % | |
| Bayshore Resilience | 33 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 160 to 171 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 195 | °C | |
| Cylinder Zone 2 Temp. | 165 to 195 | °C | |
| Cylinder Zone 3 Temp. | 165 to 195 | °C | |
| Cylinder Zone 4 Temp. | 165 to 195 | °C | |
| Cylinder Zone 5 Temp. | 165 to 195 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP BB412E | Borealis AG | PP Copolymer | Borealis PP |
| Evermore PUR SA-700 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Fainplast PVC GS 69/P | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lupol® GP3302 | LG Chem Ltd. | TPO | Lupol® |
| Pebax® MH 1657 | Arkema | PEBA-Ether | Pebax® |