Latamid 66 H2 K/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YzqU1o_Latamid-66-H2-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 to 0.85 | % | |
| Flow : 2.00 mm | 0.15 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 22500 | MPa | |
| 60°C | 22000 | MPa | |
| 90°C | 15000 | MPa | |
| 120°C | 10500 | MPa | |
| 150°C | 7700 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 220 | MPa | |
| Break, 60°C | 160 | MPa | |
| Break, 90°C | 135 | MPa | |
| Break, 120°C | 120 | MPa | |
| Break, 150°C | 100 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.7 | % | |
| Break, 60°C | 2.3 | % | |
| Break, 90°C | 3.0 | % | |
| Break, 120°C | 3.2 | % | |
| Break, 150°C | 3.4 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 85 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Capilene® QU 80 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| Etinox® ER-0000 | Ercros, S.A. | PVC, Rigid | Etinox® |
| INDURE™ X225-UV DK SHADOW | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |
| Medalist® MD-53273 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |