LUVOCOM® 2205-7123 VP Datasheet,PAEK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®2205-7123 VP is a polyaryl ketone (PAEK) material, which contains a carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 2205-7123 VP are: sterilizable Good dimensional stability chemical resistance Heat resistance Lubrication LUVOCOM®The typical application areas of 2205-7123 VP are: medical/health care

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	PTFE lubricant
Features	Good dimensional stability Good chemical resistance Heat resistance, high Hydrolysis resistance Lubrication Hydrolysis stability Disinfect with steam
Uses	Medical/nursing supplies
Appearance	Dark gray

Physical	Nominal Value	Unit	Test Method
Density	1.47	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (380°C/10.0 kg)	18	g/10 min	ISO 1133
Molding Shrinkage	0.10 - 0.40	%	DIN 16901

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	13000	MPa	ISO 527-2
Tensile Stress (Break)	145	MPa	ISO 527-2
Tensile Strain (Yield)	1.8	%	ISO 527-2
Flexural Modulus	11000	MPa	ISO 178
Flexural Stress	215	MPa	ISO 178
Coefficient of Friction
Dynamic	0.32
Static	0.29
Flexural Strain at Flexural Strength	2.3	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	250	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	26	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	220	°C	UL 746B
Vicat Softening Temperature	280	°C	ISO 306

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	3.0 - 6.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	360 - 370	°C
Middle Temperature	370 - 380	°C
Front Temperature	380 - 390	°C
Nozzle Temperature	360 - 380	°C
Processing (Melt) Temp	390	°C
Mold Temperature	160 - 180	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PAEK , Polyaryletherketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YytZ1n_LUVOCOM-2205-7123-VP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SUPREME Specialty PS SP555	Supreme Petrochem Ltd.	PS (IRPS)	SUPREME Specialty PS
Bergamid™ X2 B70 U NC	PolyOne Corporation	Nylon 6	Bergamid™
Catalyst CT/2-OR UV	Solvay Specialty Polymers	Polyolefin, Unspecified	Catalyst
Hanwha Total PP HS120	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
Lucky Enpla LGF3300	Lucky Enpla Co LTD	PBT	Lucky Enpla