Escorene™ Ultra LD 730.09 Molding
| Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Escorene™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YydLNt_Escorene-Ultra-LD-730-09-Molding.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Escorene Ultra LD 730.09 is a copolymer containing high vinyl acetate content, with low melting point, excellent strength characteristics and toughness. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 17.2 | wt% | ExxonMobil Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 15 seconds | 77 | ASTM D2240 | |
| Shaw D, 15 seconds | 34 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 640 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 55.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C | 31.2 | J | ASTM D3763 |
| 23°C | 20.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ASTM D1525 |
| Legal statement |
|---|
| 本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PA66 910/1.2 CF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| CALIBRE™ 2061-3 | Trinseo | PC | CALIBRE™ |
| EMERGE™ PC 4903 | Trinseo | PC | EMERGE™ |
| EPO-TEK® TJ1183-LH | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Pebax® 6333 SP 01 | Arkema | PEBA-Ether | Pebax® |