Badadur® PBT8 S
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YyPRqZ_Badadur-PBT8-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badadur®PBT8 S is a polybutene terephthalate (PBT) material,. This product is available in Europe,. Badadur®The main characteristics of PBT8 S are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 35 | % | ISO 527-2/50 |
| Flexural Stress (23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 4.00mm | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 4.00mm | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.018 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Additional Information |
|---|
| Short-Term Heat Resistance, IEC 216, 20000 hrs: 160°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 120°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 40 EPT2808 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Anjacom® 350-HS/GF30 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Exelene® LLDPE 2401 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |
| Hyundai EP Breathable AT820/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| Durethan® BC 304 000000 | LANXESS GmbH | Nylon 6 | Durethan® |