TECHNYL® A 218 V50 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YyEnHy_TECHNYL-A-218-V50-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218 V50 is a polyamide 66, reinforced with 50% of glass fibre, heat stabilized, for injection moulding. This product is available in natural and black colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.44 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.60 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.550 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16200 | 12500 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 220 | -- | MPa | ASTM D638 |
| Break | 240 | 175 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.0 | -- | % | ASTM D638 |
| Break | 2.0 | 2.5 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 13800 | -- | MPa | ASTM D790 |
| -- | 13500 | 10000 | MPa | ISO 178 |
| Flexural Strength | 350 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | 97 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 180 | -- | J/m | ASTM D256 |
| 23°C | 15 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 650 | -- | °C | |
| 1.60 mm | 650 | -- | °C | |
| 3.20 mm | 700 | -- | °C | |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 300 EM | RTP Company | PC | RTP |
| Shin-Etsu Elastomer KE-2090-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| NuSil CV4-2289-1 | NuSil Technology | Silicone | NuSil |
| Hanwha Total PP RB51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Hostacom EP3307 G82718 | LyondellBasell Industries | PP Copolymer | Hostacom |