SCHULAMID® 66 GBF 3020 FR 4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YwQ2Dy_SCHULAMID-66-GBF-3020-FR-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre and glass beads reinforced flame-retardant Polyamide 66 grade with low warpage high mechanical stability and high dimension stability, without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8700 | 5000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 140 | 92.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 4.5 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | -- | kJ/m² | |
| 23°C | 5.5 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 38 | -- | kJ/m² | |
| 23°C | 42 | 51 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 224 | -- | °C | ISO 75-2/Af |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 7.8E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | > 9.9E+13 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 22 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.81 | -- | ||
| 1 MHz | 3.85 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.049 | -- | ||
| 1 MHz | 0.022 | -- | ||
| Comparative Tracking Index (Solution A) | 175 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm, Self-Extinguishing) | 0.0 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 750 | -- | °C | |
| Oxygen Index | 38 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra SAN 9 | ResMart | SAN | ResMart Ultra |
| SEPAZ™ LH30 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| Teflon® PFA 440HPA | DuPont Fluoropolymers | PFA | Teflon® PFA |
| Karina GRAY PVC COMPOUND 70900-18/229-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RFL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |