Rilsan® CLEAR G 350
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yw793y_Rilsan-CLEAR-G-350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G350 is a high performance transparent copolyamide. This grade has been specially designed for injection molding applications, ideally suited for applications such as high end eyewear frames. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 40°C, 24 hr, 4.00 mm | 0.64 | % | |
| Flow : 40°C, 24 hr, 4.00 mm | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 3.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 81 | ||
| Shore D, 15 sec | 78 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1480 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 51.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | > 150 | % | |
| Flexural Modulus | 1340 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Glass Transition Temperature | 145 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 91.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 20.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTOSIL® LR 3004/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LEXAN™ LUX2110T_ resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 750D35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® NA340163 | LyondellBasell Industries | LDPE | Petrothene® |
| Hifax 5519/1 G 1750 | LyondellBasell Industries | PP Copolymer | Hifax |