CoolPoly® E3603
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yw0pIU_CoolPoly-E3603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly E series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The E series is electrically conductive and provides inherent EMI/RFI shielding charactersitics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9070 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 44.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.56 | % | ISO 527-2 |
| Flexural Modulus | 9840 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 4.7 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 20 | W/m/K | ASTM E1461 |
| Heat Capacity | 1050 | J/kg/°C | ASTM E1461 |
| Thermal Diffusivity | 0.120 | cm²/s | ASTM E1461 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 12 - 24 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 300 - 315 | °C | |
| Front Temperature | 305 - 325 | °C | |
| Nozzle Temperature | 290 - 315 | °C | |
| Processing (Melt) Temp | 310 - 325 | °C | |
| Mold Temperature | 107 - 163 | °C | |
| Injection Pressure | 6.90 - 10.3 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 3.45 - 6.90 | MPa | |
| Back Pressure | 0.00 - 0.350 | MPa | |
| Screw Speed | 50 - 150 | rpm | |
| Cushion | 6.30 - 12.7 | mm | |
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Drying ConditionsStarting Moisture Content 0.05 to 0.2%: 2 to 4 hr at 80°C 0.2 to 0.5%: 4 to 8 hr at 80°C >0.5% or unknown: 12 to 24 hr at 104°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PQ 83 T 20 | Plastcom | PP+EPDM | SLOVALEN® |
| Lupox® LW5102F | LG Chem Ltd. | PC+PBT | Lupox® |
| Plaslube® POM CO E TL20 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| SIBUR Synthetic Rubber IR SKI-3 NST Group II | SIBUR | IR | SIBUR Synthetic Rubber |
| Durethan® AC 30 DUS027 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |