Smooth-Cast® 385
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-Cast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YvK440_Smooth-Cast-385.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Smooth-Cast® 385 is a mineral filled urethane casting resin that is very hard and durable. When Parts A and B are mixed in proper proportion (1A:5B by weight), Smooth-Cast® 385 cures at room temperature with virtually no shrinkage. This rigid urethane casting resin has high compressive and flexural strength. Fully cured castings are tough, machinable and paintable. Color effects are possible by adding pigment dispersions. They resist moisture and mild solvents. Smooth-Cast® 385 is ideal for making industrial production parts, foundry patterns, vacuum forming molds, and some ceramic applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.625 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:5B by weight |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.060 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength (Break) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 2990 | MPa | ASTM D790 |
| Flexural Strength | 40.7 | MPa | ASTM D790 |
| Compressive Modulus | 2760 | MPa | ASTM D695 |
| Compressive Strength | 58.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.2 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 20 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 3000 | cP | ASTM D2393 |
| Demold Time (23°C) | 120 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A121U GR20-50 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| Axiall PVC 10753 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Epoxies, Ect. 20-2621 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| INSTRUC PPGF15FC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |
| Hifax HSBM CB 1157 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |