LNP™ THERMOCOMP™ OF008E compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YvGy6c_LNP-THERMOCOMP-OF008E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008E is a compound based on PPS - Linear resin containing 40% Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound OF-1008 EM Product reorder name: OF008E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 | % | |
| Across Flow : 24 hr | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 179 | MPa | ASTM D638 |
| Break | 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.7 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14300 | MPa | ASTM D790 |
| -- | 13400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 248 | MPa | ASTM D790 |
| -- | 190 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.66 | ||
| vs. Itself - Static | 0.87 | ||
| Wear Factor - Washer | 240 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 1 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 272 | °C | ISO 75-2/Af |
| CLTE - Flow (-40 to 40°C) | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicostirolo P165 | Ravago Group | PS (HIPS) | Sicostirolo |
| Tenite™ Propionate 358A4000018 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Spartech Polycom SS1080U | Spartech Polycom | ASA | Spartech |
| TEREZ PA 6 7950 HI | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Zetpol® 0020EP | Zeon Chemicals L.P. | NBR | Zetpol® |