KPOL-HDPE HD K-0.17/951

Category:	HDPE , High Density Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YuwMyI_KPOL-HDPE-HD-K-0-17-951.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene Copolymer HMW Extrusion-Blow Molding

Applications

Bottles for home use chemical liquid substances (bleache) and industrial chemicals (lubricants) up to 10 litters.

Bottles containing liquids for personal use (shampoo). Bottles for pharmaceutical products.

Characteristics

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable High Density High Molecular Weight
Uses	Bottles
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.951	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/2.16 kg	0.17	g/10 min
190°C/21.6 kg	13	g/10 min
Environmental Stress-Cracking Resistance			ASTM D1693B
60°C, 10% Igepal CO-630, F50 ¹	> 500	hr
50°C, 1.90 mm, 100% Igepal CO-630, F50 ²	58.0	hr

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	68		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ³(Yield)	27.6	MPa	ASTM D638
Tensile Elongation ⁴(Break)	600	%	ASTM D638
Flexural Modulus - Tangent ⁵(3.20 mm)	1380	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.20 mm)	270	J/m	ASTM D256A
Tensile Impact Strength	242	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	75.0	°C	ASTM D648
Brittleness Temperature ⁶	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	125	°C	ASTM D1525 ⁷
Melting Temperature	129	°C	DSC

Note Message
1 .	16 oz cylindrical bottle (approximated mass of 20 g) filled up to 33% of its capacity
2 .	Grooved Specimen
3 .	Type IV, 50 mm/min
4 .	Type IV, 50 mm/min
5 .	13 mm/min
6 .	F50; 25 lbfXin
7 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RANPELEN J-550A	Lotte Chemical Corporation	PP Random Copolymer	RANPELEN
ACCUTECH™ CP0437G5M25CL	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™
KIBILAC® PW-997G	CHI MEI CORPORATION	ASA	KIBILAC®
Osterlene® PPH-30-.4	Osterman & Company	PP Homopolymer	Osterlene®
3M™ Dyneon™ Fluoroelastomer FC 2124	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer