ELITE™ 5500G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YurDvW_ELITE-5500G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE* 5500G Enhanced Polyethylene Resin is a copolymer produced via INSITE* Technology. It offers an exceptional combination of processability, low heat seal initiation temperature, package integrity, optical properties, and tear strength.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.914 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 5.65 | J | Internal method |
| Film Puncture Force | 62.3 | N | Internal method |
| Film Puncture Resistance | 29.0 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 91.0 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 162 | MPa | ASTM D882 |
| 2% secant, MD | 141 | MPa | ASTM D882 |
| 1% secant, TD | 193 | MPa | ASTM D882 |
| 2% secant, TD | 165 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 18.3 | MPa | ASTM D882 |
| TD : Yield | 10.3 | MPa | ASTM D882 |
| MD : Fracture | 41.4 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 400 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Dart Drop Impact | 650 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 350 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 45 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 226 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：425°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：42 rpm 冷冻线高度：47 英寸 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ESTAPROP 1050 V0 HF K | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Fainplast PVC RH 214 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hanwha Total PP FB54NH | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| IROGRAN® A 85 E 4993 FCM | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina COMP. PVC WHITE -E 800-10/ 1-CY-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |