Order Products : sales@su-jiao.com
INNOPOL® PP CS 2-7120
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YuiUGY_INNOPOL-PP-CS-2-7120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INNOPOL® CS 2-7120 is a 20 % talc-filled polypropylene block copolymer compound / PP-B TD20 (ISO 1043)/. This grade is available in nature and custom coloured form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 102 | °C | ISO 75-2/B |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Cylinder Zone 1 Temp. | 180 to 220 | °C | |
| Cylinder Zone 2 Temp. | 180 to 220 | °C | |
| Cylinder Zone 3 Temp. | 180 to 220 | °C | |
| Cylinder Zone 4 Temp. | 180 to 220 | °C | |
| Cylinder Zone 5 Temp. | 180 to 220 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Die Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P55A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| TRILOY® TP210T | Samyang Corporation | PC+ABS | TRILOY® |
| Exceed™ XP 8358ML | ExxonMobil Chemical | PP Elastomer | Exceed™ XP |
| Sylvin 9604A-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® B 40 FKA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |