Rilsan® BESNO P210 TL
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YuOhoK_Rilsan-BESNO-P210-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESNO P210 TL is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion. BESNO P210 TL falls into the PA11-PHLY category according to DIN 73378 and fulfils all specifications according to DIN 74324, ISO 7628, NFR 12632, and SAE J844. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 75 | ||
| Shore D, 15 sec | 67 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 590 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 30.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 35 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 450 to 600 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 184 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-HIP, EHL, 22-005 | ISO 1874 | |
| Renewable Carbon Conent | > 89 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 5 Series 598A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| APEX® 3708-85NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC MGS 87/GT | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KOCETAL® GF706BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Polene EVA N 8036 | TPI Polene Public Company Limited | EVA | Polene EVA |