MARPOL® LL6R 802
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yu6REQ_MARPOLLL6R802.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MARPOL LL6R 802 is a polyethylene resin designed for rotational applications that require high stiffness, exceptional low temperature impact properties and excellent ESCR performance. This resin is UV stabilized, has a broad processing window and superior whiteness for improved part appearance. Recommended Applications: Very large tanks, septic and agricultural tanks |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.942 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | < 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 1030 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 62.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 42.8 | °C | ASTM D648 |
| Melting Temperature | 127 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205D TFE 15 Z | RTP Company | Nylon 612 | RTP |
| ABSCOM® T4060 | Polymer Compounders Limited | ABS | ABSCOM® |
| Hyflon® PFA M620 | Solvay Specialty Polymers | PFA | Hyflon® PFA |
| Karina WHITE PVC COMPOUND -E 836-10/185-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoElast S A9000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |