Luran® S 767KE
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Styrolution |
| Trademark: | Luran® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ytzlmo_Luran-S-767KE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran S 767KE is particular suitable for co-extrusion with PVC at low temperature. Hereby, it provides a glossy surface finish. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.59 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.90 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | 0.35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 80.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.3 | % | ISO 527-2 |
| Tensile Creep Modulus (1000 hr) | 1400 | MPa | ISO 899-1 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 8.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 98.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 3.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.011 | ||
| 1 MHz | 0.024 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Note Message | |
|---|---|
| 1 . | With external lubricant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-84348 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist® |
| Synres-Almoco EP 3536 | Synres-Almoco BV | Epoxy | Synres-Almoco |
| VICTREX® PEEK 450G903 Black | Victrex plc | PEEK | VICTREX® PEEK |
| Torelina® A900 | Toray Resin Company | PPS | Torelina® |
| Elvaloy® AC 3117 | DuPont Packaging & Industrial Polymers | EnBA | Elvaloy® |