Glastic® SG-200
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Glastic Corporation |
| Trademark: | Glastic® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ysrkb1_Glastic-SG-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glastic SG-200 high-strength and high-temperature laminate offers the same high-performance features and benefits as Glastic's FHT Laminate. In addition, SG-200 offers much higher mechanical strengths than FHT with temperature ratings of up to 210°C. Glastic SG-200 is also a superior replacement material for epoxy-bonded mica in layer insulation applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.60 mm) | 11700 | MPa | ASTM D638 |
| Tensile Strength (yield, 1.60mm) | 86.2 | MPa | ASTM D638 |
| Flexural Strength (yield, 1.60mm) | 200 | MPa | ASTM D790 |
| Compressive Strength (1.60 mm) | 248 | MPa | ASTM D695 |
| Shear Strength | 76.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (1.60 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (1.60 mm) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| RTI Elec (1.60 mm) | 210 | °C | UL 746 |
| RTI (1.60 mm) | 210 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.5E+10 | ohms | ASTM D257 |
| Dielectric Strength 1 | ASTM D149 | ||
| 1.60 mm, in Air | 20 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 25 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1.60 mm, 60 Hz | 4.60 | ASTM D150 | |
| 1.60 mm, 1 MHz | 3.70 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1.60 mm, 60 Hz | 0.037 | ASTM D150 | |
| 1.60 mm, 1 MHz | 0.013 | ASTM D150 | |
| Arc Resistance (1.60 mm) | 120 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (1.60 mm) | 500 | V | UL 746 |
| High Amp Arc Ignition (HAI) (1.60 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.60 mm) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.711 mm | 35 | sec | UL 746 |
| 1.47 mm | 39 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index (1.60 mm) | 22 | % | ASTM D2863 |
| Additional Information |
|---|
| NEMA Grade: GPO-1Insulation Resistance, ASTM D257: 1.45e10 ohms |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound NH3022S | Samyang Corporation | PC | TRIREX® Compound |
| XYRON™ L564V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Mylar® MO (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Geon™ 170 Series L100UF | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 170 Series |
| EPAMOULD 660D12G20 | Epaflex Polyurethanes S.R.L. | TPU, Unspecified | EPAMOULD |