Ducor® 1100 S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | Ducor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YsoHhv_Ducor1100S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ducor 1100S is a homopolymer, characterized by high flowability and medium molecular weight distribution, and is formulated with a general-purpose additive package. Ducor 1100S is used for general injection moulding applications. Food Contact Applications: This grade is in compliance with most regulations regarding food contact applications (EU, FDA). Specific information is available upon request. Applications Closures, furniture, housewares, general IM |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 78.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | ISO 527-2/50 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Shear Modulus | 800 | MPa | ISO 6721-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 1.3 | kJ/m² | ISO 180/1A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 90.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm, Injection Molded) | 60 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® E3400 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Amilan® CM3001R | Toray Resin Company | Nylon 66 | Amilan® |
| Formolene® HP5221 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Plasmer 5050D-1/3839 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |