Sindustris PC SC5005T
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ysg66o_Sindustris-PC-SC5005T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC SC5005T is a Polycarbonate + Polyester (PC+Polyester) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC SC5005T are:
Typical application of Sindustris PC SC5005T: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 60.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 97.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 123 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 265 to 295 | °C | |
| Processing (Melt) Temp | 265 to 290 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 20 Z | RTP Company | Nylon 66 | RTP |
| RTP 199 X 130883 B | RTP Company | PP, Unspecified | RTP |
| Spartech Polycom PP5340 | Spartech Polycom | PP Homopolymer | Spartech |
| Bayfill® 53IF40 U | Covestro - PUR | PUR, Unspecified | Bayfill® |
| SABIC® PPcompound 1961 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |