Andur M-33 (HQEE) Datasheet,PUR-Ester/MDI,Anderson Development Company-SHANGHAI SUSHENG

Message
Andur M-33 is a low melting MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in low temperature applications.

General Information
Forms	Liquid

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw A	96	ASTM D2240
Shaw D	42	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Compressive Strength			ASTM D695
2% strain	0.621	MPa	ASTM D695
5% strain	2.69	MPa	ASTM D695
10% strain	4.14	MPa	ASTM D695
15% strain	5.45	MPa	ASTM D695
20% strain	6.76	MPa	ASTM D695
25% strain	8.20	MPa	ASTM D695
50% strain	26.7	MPa	ASTM D695
Taber Abrasion Resistance	29.0	mg	ASTM D1044

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
100% strain	12.2	MPa	ASTM D412
300% strain	14.8	MPa	ASTM D412
Tensile Strength (Yield)	18.4	MPa	ASTM D412
Tensile Elongation (Break)	510	%	ASTM D412
Compression Set	21	%	ASTM D395
Bayshore Resilience	45	%	ASTM D2632

Thermoset	Nominal Value	Unit
Pot Life	6.0 - 8.0	min
Demold Time	45	min

Additional Information
Die C Tear, ASTM D1004: 695 pliAverage Split Tear, ASTM D1938: 170 pliStoichiometry Curative Level: 97%NBS Abrasion: 240% Rubber StandardParts of curative per 100 parts Andur M-33, 6.75% NCO: 15.15 parts by weightParts of curative per 100 parts Andur M-33, 6.8% NCO: 15.26 parts by weightParts of curative per 100 parts Andur M-33, 6.85% NCO: 15.38 parts by weightParts of curative per 100 parts Andur M-33, 6.9% NCO: 15.49 parts by weightParts of curative per 100 parts Andur M-33, 6.95% NCO: 15.6 parts by weightParts of curative per 100 parts Andur M-33, 7% NCO: 15.71 parts by weightMix Temperature: Andur M-33: 212°F Curative HQEE: 77-158°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours

Additional Information

Die C Tear, ASTM D1004: 695 pliAverage Split Tear, ASTM D1938: 170 pliStoichiometry Curative Level: 97%NBS Abrasion: 240% Rubber StandardParts of curative per 100 parts Andur M-33, 6.75% NCO: 15.15 parts by weightParts of curative per 100 parts Andur M-33, 6.8% NCO: 15.26 parts by weightParts of curative per 100 parts Andur M-33, 6.85% NCO: 15.38 parts by weightParts of curative per 100 parts Andur M-33, 6.9% NCO: 15.49 parts by weightParts of curative per 100 parts Andur M-33, 6.95% NCO: 15.6 parts by weightParts of curative per 100 parts Andur M-33, 7% NCO: 15.71 parts by weightMix Temperature: Andur M-33: 212°F Curative HQEE: 77-158°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours

Injection	Nominal Value	Unit
Mold Temperature	110 - 140	°C

Category:	PUR-Ester/MDI , Polyurethane (Polyester, MDI)
Manufacturer:	Anderson Development Company
Trademark:	Andur
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ys0x5M_Andur-M-33-HQEE-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
CPI PP 40 Natural	CPI Binani, Inc.	PP, Unspecified	CPI PP
DEXFLEX® 810-1	LyondellBasell Industries	TPO (POE)	DEXFLEX®
Elastron® V V201.A78.B	Elastron USA, Inc.	TPV	Elastron® V
PETILEN I 668	PETKIM Petrokimya Holding A.S.	HDPE	PETILEN
LEXAN™ XHT3141 resin	SABIC Innovative Plastics	PC	LEXAN™